| Application examples include aerospace counterweights (requiring high precision and density), medical shielding components (requiring surface finish and corrosion resistance), and drilling tools (requiring wear resistance). Optimization should be adjusted according to target performance. For example, HIP and nickel plating for medical parts, while drilling tools emphasize carburizing and coating. | |||
| Technology Category | Key Method | Typical Parameters | Target / Effect |
| Machining | Turning | 40-60 m/min, 0.1 mm/r | Surface roughness Ra 1.6 μm |
| Grinding | 20-30 m/s, Ra 0.4 μm | High-precision surface | |
| Heat Treatment | Annealing | 900°C, 2 hours | Stress reduced to 50 MPa, elongation +10% |
| Aging | 600°C, 4 hours | Strength 1100 MPa, hardness 480 HV | |
| Surface Treatment | Nickel Plating | 5 μm thick | Corrosion rate reduced to 0.2% |
| Carburizing | 950°C, 3 hours | Hardness 600 HV, wear resistance +30% | |
| Joining Technology | Electron Beam Welding | 5 kW, 1 m/min | Weld strength 90% |
| Brazing | 850°C, Ag-Cu filler metal | Shear strength 200 MPa | |
| Post-processing Optimization | HIP | 200 MPa, 1400°C | Porosity 0.1%, service life +50% |
| Laser Etching | Micro-pores 50 μm | Friction coefficient +20% | |
| Note: The table data is based on typical processes of our experience, specific values may vary according to application requirements. | |||